%T Growth and Properties of Large Single Crystals of YBa2Cu3O7-d from BaCuO2/CuO Flux
%J Australian Journal of Physics
%D 1991/06/01
%V 44
%N 4
%P 421-428
%K 
%R https://doi.org/10.1071/PH910421
%U https://www.publish.csiro.au/paper/PH910421 
%X Large single crystals of YBa2Cu307-o have been grown using a BaCu02/CUO flux whose composition lies close to the eutectic in the Y-Ba-Cu-o phase diagram. While the largest crystals produced were '" 20x20xO· 7 mm3, the average size of the remaining crystals was approximately 10x10xO· 5 mm3. These crystals, both as-grown and oxygen annealed, have been characterised using susceptibility measurements, optical and scanning microscopy and X-ray and neutron diffraction techniques. 